This is the above weld close-up. It looks like to me either argon starvation or if not that then argon cooling the weld too much to make it a useful weld.

The weld beads(or balls rather in this case) aren't welded to the base piece at all. I can break them off easily with the screw driver.

https://youtu.be/mfYLnXJT6JE